Grade : K10
Grade with good wear resistance for general machining of cast irons, aluminum & non-ferrous materials, and heat-resistant alloy

PropertyValue
ISO Range - P/M/K(K05-K15)
ISO Range - H/S/N (S05-S15)(N05-N15)
HRA92
Coating TypeUN-COATED
Coating LayerUncoated



Cutting Speed for: TIPV 3.18 0.20 K10 - 6450223
ISOMaterialMaterial DescriptionMaterial ConditionCutting Speed Recommendations
K15Grey cast iron (GG)Pearlitic/ferritic :180100-140 m/min
K16Grey cast iron (GG)Pearlitic/martensiti :26090-130 m/min
K17Nodular cast iron (GGG)Ferritic :160110-150 m/min
K18Nodular cast iron (GGG)Pearlitic :25090-130 m/min
K19Malleable cast iron.Ferritic :130100-140 m/min
K20Malleable cast iron.Pearlitic :23090-130 m/min
N21Aluminum-wrought alloy.Not cureable : 60550-700 m/min
N22Aluminum-wrought alloy.Cured :100600-750 m/min
N23Aluminum-cast, alloyed <12% Si.Not cureable : 75800-900 m/min
N24Aluminum-cast, alloyed.Cured : 90650-800 m/min
N25Aluminum-cast, alloyed >12% Si.High temperature :130250-350 m/min
N26Copper alloys >1% pb.Free cutting :110300-400 m/min
N27Copper alloys.Brass : 90300-400 m/min
N28Copper alloys.Electrolitic copper :100210-280 m/min
N29Non metallic.Duro& fiber plastics : 60150-250 m/min
N30Non metallicHard rubber : 55150-250 m/min
S31High temp. alloys Fe based.Annealed :20050-70 m/min
S32High temp. alloys Fe based.Cured :28040-50 m/min
S33High temp. alloys. Ni or Co based.Annealed :25050-60 m/min
S34High temp. alloys. Ni or Co based.Cured :35035-40 m/min
S35High temp. alloys. Ni or Co based.Castr :32045-50 m/min
S36Titanium (pure):31020-45 m/min
S37Titanium Ti alloys.Alpha+beta alloys cu :31035-45 m/min
H38Hardened steel.Hardened :5608-12 m/min
H39Hardened steel.Hardened :6546-10 m/min
H40Chilled cast iron.Cast :40015-25 m/min
H41Cast iron.Hardened :5608-12 m/min