Grade : TT5505

PVD AlTiN coated grade on ultra-fine substrate with high wear resistance and oxidation resistance for high speed machining of hardened steels and pre-hardened alloys of hardness under 65 HRC

Property	Value
ISO Range - P/M/K	(P05-P25)
ISO Range - H/S/N	(H05-H25)

Property	Value
Grade or Coating Type	PVD
Coating Layers	AlTiN
Grade Color	BROWN

Cutting Speed for: HSF 6030M 080 TT5505 - 6127474

ISO	Workpiece Material Group	Material Designation	Material Condition	Hardness	Cutting Speed Recommendations (Vc)
P	1	Non-alloy steel and cast steel, free cutting steel <0.25%C.	Annealed	125 HB	260-300 m/min
P	2	Non-alloy steel and cast steel, free cutting steel >=0.25%C.	Annealed	190 HB	200-250 m/min
P	3	Non-alloy steel and cast steel, free cutting steel <0.55%C.	Quench and tempered.	250 HB	160-230 m/min
P	4	Non-alloy steel and cast steel, free cutting steel >=0.55%C.	Annealed	220 HB	160-230 m/min
P	5	Non-alloy steel and cast steel, free cutting steel >=0.55%C.	Quenched & tempered.	300 HB	140-200 m/min
P	6	Low alloy & cast steel (less than 5% of alloying elements).	Annealed	200 HB	160-230 m/min
P	7	Low alloy & cast steel (less than 5% of alloying elements).	Quenched & tempered	275 HB	120-200 m/min
P	8	Low alloy & cast steel (less than 5% of alloying elements).	Quenched & tempered	300 HB	140-200 m/min
P	9	Low alloy & cast steel (less than 5% of alloying elements).	Quenched & tempered	350 HB	140-200 m/min
P	10	High alloyed steel, cast steel and tool steel.	Annealed	200 HB	140-200 m/min
P	11	High alloyed steel, cast steel and tool steel.	Quenched & tempered	325 HB	80-150 m/min
K	15	Grey cast iron (GG)	Pearlitic/ferritic	180 HB	100-300 m/min
K	16	Grey cast iron (GG)	Pearlitic/martensiti	260 HB	130-280 m/min
K	17	Nodular cast iron (GGG)	Ferritic	160 HB	150-280 m/min
K	18	Nodular cast iron (GGG)	Pearlitic	250 HB	90-280 m/min
K	19	Malleable cast iron.	Ferritic	130 HB	150-280 m/min
K	20	Malleable cast iron.	Pearlitic	230 HB	140-250 m/min
S	31	High temp. alloys Fe based.	Annealed	200 HB	20-40 m/min
S	32	High temp. alloys Fe based.	Cured	280 HB	20-30 m/min
S	33	High temp. alloys. Ni or Co based.	Annealed	250 HB	20-30 m/min
S	34	High temp. alloys. Ni or Co based.	Cured	350 HB	20-30 m/min
S	35	High temp. alloys. Ni or Co based.	Cast	320 HB	30-80 m/min
H	38	Hardened steel.	Hardened	55 HRC	30-60 m/min
H	39	Hardened steel.	Hardened	60 HRC	30-40 m/min
H	40	Chilled cast iron.	Cast	400 HB	70-90 m/min
H	41	Cast iron.	Hardened	55 HRC	30-60 m/min